Accident to the AIRBUS A380-861 registered F-HPJE and operated by Air France on 30/09/2017 en route over Greenland [Investigation delegated to BEA by the authorities of Denmark]

BEA published its final report about the incident.

https://www.bea.aero/en/investigation-r … 17-en-cro/

SUMMARY

On Saturday, 30 September 2017, the Airbus A380-861 operated by Air France, was carrying out scheduled flight AF066 from Paris (France) to Los Angeles (USA). It took off at 09:50. At 13:49, while the crew were changing en-route flight level, they heard an explosion and observed asymmetric thrust from the right side of the aeroplane, immediately followed by severe vibrations. The “ENG 4 STALL” and then the “ENG 4 FAIL” messages nearly simultaneously appeared on the ECAM. The crew diverted to Goose Bay airport (Canada) where they landed at 15:42 without any further incident.

A visual examination of the engine found that the fan, first rotating assembly at the front of the engine, along with the air inlet and fan case had separated in flight leading to slight damage to the surrounding structure of the aircraft.

The factors likely to have contributed to the accident include:

• engine designer’s/manufacturer’s lack of knowledge of the cold dwell fatigue phenomenon in the titanium alloy, Ti-6-4;
• absence of instructions from the certification bodies about taking into account macro-zones (i.e. colony of similarly oriented alpha grains) and the cold dwell fatigue phenomenon in the critical parts of an engine, when demonstrating conformity;
• absence of non-destructive means to detect the presence of unusual macro?zones in titanium alloy parts;
• an increase in the risk of having large macro-zones with increased intensity in large Ti-6-4 forgings due to bigger engines, and in particular, bigger fans.

After the accident, regular inspections of the fleet in service found that there were no cracks detected in the areas considered at risk on the fan hubs of the Engine Alliance engines equipping the A380. The certification bodies and engine manufacturers are currently considering how to better understand the cold dwell fatigue phenomenon and take it into account in the design of future engines.